HG-S.3000 single component. Neutral ketoxime type curing, medium modulus, durable, no corrosion on the substrate surface, excellent bonding and sealing function for most materials, high weather resistance aluminum alloy door and window sealant.
Applicable materials: Suitable for the combined assembly and sealing of commonly used building materials such as glass, ceramics, fiberglass, galvanized metal surfaces, pottery, most plastic panels, non-oily wood, anodized or painted aluminum profiles.
Use restrictions: Not suitable for engineering applications where the surface temperature of the construction substrate exceeds 50°C, and it cannot be used in an environment that is completely isolated from air before curing.
PERFORMANCE DATA | |||
Test Parameter | Unit | Result Translucent Pigmented | |
As Supplied Tested at 23ºC and 50% RH | |||
Specific Gravity | g/ml | 1.21±0.02 | 1.52±0.02 |
Flow (sag or slump) | mm | 0 | 0 |
Extrusion Rate | ml/minute | 135 | 103 |
Skin Time | minute | 5~10 | ≤95 |
Tack-free Time | hour | ≤1.0 | ≤12 |
Curing time (5mm) | hour | ≤12 | ≤19 |
As Cured-after 21 days at 23ºC and 50% RH | |||
Durometer Hardness, Shore A | Points | 23 | 31 |
Elastic Recovery | % | 92 | 90 |
Movement Capability | % | ±22 | ±20 |
Tensile/Modulus at 50% Elongation | % | 0.22 | 0.45 |
Tensile/Modulus at 100% Elongation | % | 0.31 | 0.56 |
Ultimate Tensile Strength | Mpa | 0.32 | 0.62 |
Ultimate Elongation at Break | % | 180 | 380 |