Customization: | Available |
---|---|
CAS No.: | 68928-70-1 |
Formula: | C36h32br8o6 |
Still deciding? Get samples of US$ 0.01/Piece
Request Sample
|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Basic Info. | |||
Model NO. | HW-low modulus ms sealant | Material | Modified polyether |
Classification | Room Curing | Main Agent Composition | polyether |
Characteristic | Environmental friendly | Promoter Composition | Curing Agent |
Composition | Mixture | Color | Black |
OEM | Avaliable | Packing | 20or24 PCS in a Carton |
Function | Bonding Sealing Caulking Waterproofing | Cetificate | ISO 9001: 2015 |
Market | Global | Shelf Life | 18 Months |
Usage | Caulking, sealing and bonding | Transport Package | Ocean Shipping |
Specification | 300ml,600ml | Trademark | HW |
Origin | China | Production Capacity | 20000 Piece/Pieces Per Day |
sink time | 30min | fully cured | 3mm/24Hours |
Shore hardness A | 36 | 100% elastic modulus | 0.75N/MM2 |
MS polymer sealant technical parameters | ||
NO. | Test items | Test Data |
1 | Exterior | The color is in accordance with the technical requirements, the state is uniform, paste-like, no particles, no bubbles, no impurities. |
2 | solid content | 99.02 |
3 | Density g/ml | 1.47±0.01 |
4 | Tack drying time: 23ºC, 50% | 60±5 |
5 | Curing depth mm/24 hours | 1.9 |
6 | Curing depth mm/7 days | 4.9 |
7 | Glass adhesion and cohesive damage | ok |
8 | Concrete adhesion and cohesive failure | ok |
9 | Shore hardness A | 29±2 |
10 | Thin consistency | 8.6±0.1 |
11 | Tensile strength (curing 7 days) Mpa | 1.45 |
12 | Elongation at break (curing 7 days) % | 680 |
13 | Shear strength 7 days | 0.82 |
14 | Shear strength 14 days | 0.9 |
15 | Storage period, double 70, 7d/14d | ok |