**HC-888 Premium Acidic-Curing Silicone Glass Sealant**
**Product Overview**
The HC-888 is a high-performance, single-component acidic-curing silicone adhesive designed for superior bonding and sealing in advanced glass and aluminum projects. Perfect for aquariums, large glass panels, sophisticated glass engineering, lighting ceilings, and aluminum alloy glass doors and windows, HC-888 delivers exceptional durability and professional-grade performance for demanding applications.
### **Key Features**
- **Exceptional Versatility:** Suitable for a wide range of materials, including:
- Glass
- Ceramics
- Fiberglass
- Non-oily wood
- Aluminum profiles
- Painted surfaces
- **Enhanced Application:** For powder-coated aluminum alloy surfaces, ensure complete removal of surface coating wax with a solvent to achieve optimal adhesion.
- **Professional Reliability:** Engineered for precise, high-quality results, HC-888 provides robust adhesion and long-lasting seals for diverse construction and decorative needs.
### **Usage Guidelines**
To ensure the best performance, please adhere to the following usage restrictions:
- **Material Compatibility:** Not suitable for concrete, cement, structural components, or substrates containing zinc, brass, copper, or lead.
- **Environmental Considerations:** Avoid continuous immersion in water or application in fully air-isolated environments before curing.
- **Specialized Applications:** Not recommended for surfaces requiring painting or projects needing architectural-grade engineering sealants.
### **Shelf Life**
The HC-888 offers a **12-month shelf life** under proper storage conditions, ensuring consistency and reliability for your projects.
With its exceptional adhesive properties and superior performance, HC-888 is the trusted choice for advanced glass installations and aluminum bonding. Rely on HC-888 for flawless results in even the most demanding glass and aluminum projects.
PERFORMANCE DATA | ||
Test Parameter | Unit | Result |
As Supplied Tested at 23ºC and 50% RH | ||
Specific Gravity | g/ml | 0.98±0.02 |
Flow (sag or slump) | mm | 0 |
Extrusion Rate | ml/minute | 180 |
Skin Time | minute | 5~10 |
Tack-free Time | hour | ≤1.0 |
Curing time (5mm) | hour | ≤10 |
As Cured-after 21 days at 23ºC and 50% RH | ||
Durometer Hardness, Shore A | Points | 30 |
Movement Capability | % | 35 |
Tensile/Modulus at 50% Elongation | Mpa | 0.45 |
Tensile/Modulus at 100% Elongation | Mpa | 0.5 |
Ultimate Tensile Strength | Mpa | 0.52 |
Ultimate Elongation at Break | % | 465 |