**HG-S.2000 Premium Acidic-Curing Silicone Glass Sealant**
**Product Overview**
The HG-S.2000 is a high-performance, single-component acidic-curing silicone glass sealant, designed to meet the demands of large-scale and advanced glass projects. Its robust formulation ensures superior adhesion and sealing performance, making it the ideal choice for applications such as large glass installations, lighting ceilings, aluminum alloy glass doors and windows, and large window assemblies. Engineered for professional use, HG-S.2000 delivers reliability and durability for even the most demanding projects.
### **Key Features**
- **Acidic-Cure Technology:** Provides fast curing with exceptional bonding strength for advanced applications.
- **Versatile Application:** Designed for large glass projects, lighting ceilings, and aluminum alloy installations.
- **Durability:** Ensures long-lasting sealing performance in diverse environments.
- **Professional Grade:** Trusted by construction professionals for its consistent, high-quality results.
### **Applicable Materials**
HG-S.2000 is compatible with a variety of materials, including:
- Glass
- Ceramics
- Fiberglass
- Non-oily wood
- Aluminum profiles
- Painted material surfaces
**Important Note:** For aluminum alloy surfaces treated with powder coating, ensure complete removal of surface coating wax using a solvent before application to achieve optimal adhesion.
### **Usage Restrictions**
To maintain peak performance, avoid the following applications:
- **Incompatible Materials:** Not suitable for concrete, cement, or substrates containing zinc, brass, copper, or lead.
- **Curing Limitations:** Avoid continuous immersion in water or application in fully air-isolated environments before curing.
- **Specialized Applications:** Not recommended for surfaces requiring painting or for use as architectural-grade structural sealants.
### **Shelf Life**
HG-S.2000 retains its superior performance for up to **12 months** when stored under recommended conditions.
**Why Choose HG-S.2000?**
With its advanced acidic-curing technology and professional-grade performance, HG-S.2000 is the trusted solution for large glass and aluminum projects. Its exceptional durability, strong adhesion, and versatile application make it the ideal choice for professionals tackling demanding sealing and assembly tasks. Trust HG-S.2000 for flawless results and long-term reliability in your most challenging projects.
| PERFORMANCE DATA | ||
| Test Parameter | Unit | Result |
| As Supplied Tested at 23ºC and 50% RH | ||
| Specific Gravity | g/ml | 0.96±0.02 |
| Flow (sag or slump) | mm | 0 |
| Extrusion Rate | ml/minute | 150 |
| Skin Time | minute | 5~10 |
| Tack-free Time | hour | ≤1.0 |
| Curing time (5mm) | hour | ≤12 |
| As Cured-after 21 days at 23ºC and 50% RH | ||
| Durometer Hardness, Shore A | Points | 22 |
| Movement Capability | % | 30 |
| Tensile/Modulus at 50% Elongation | Mpa | 0.31 |
| Tensile/Modulus at 100% Elongation | Mpa | 0.35 |
| Ultimate Tensile Strength | Mpa | 0.42 |
| Ultimate Elongation at Break | % | 375 |