CAS No.: | 63148-60-7 |
---|---|
Formula: | C16h22o2si2 |
EINECS: | 51852-81-4 |
Bonding Function: | Structural Adhesive |
Morphology: | Paste |
Application: | Automobile, Construction, Woodworking |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
HG-S.9500 Single Component Acidic Curing Silicone Glass Glue is designed for a variety of applications including aquariums, large plate glass, advanced glass engineering, lighting ceilings, and the installation of various aluminum alloy glass doors and windows, as well as large window assembly and sealing projects.
Key Features:
Applicable Materials: This glue is suitable for bonding a variety of materials, including:
Note: Aluminum alloy sprayed with powder must have the surface coating wax completely removed with a solvent before use.
Usage Restrictions:
PERFORMANCE DATA | ||
Test Parameter | Unit | Result |
As Supplied Tested at 23ºC and 50% RH | ||
Specific Gravity | g/ml | 0.98±0.02 |
Flow (sag or slump) | mm | 0 |
Extrusion Rate | ml/minute | 180 |
Skin Time | minute | 5~10 |
Tack-free Time | hour | ≤1.0 |
Curing time (5mm) | hour | ≤10 |
As Cured-after 21 days at 23ºC and 50% RH | ||
Durometer Hardness, Shore A | Points | 30 |
Movement Capability | % | 35 |
Tensile/Modulus at 50% Elongation | Mpa | 0.45 |
Tensile/Modulus at 100% Elongation | Mpa | 0.5 |
Ultimate Tensile Strength | Mpa | 0.52 |
Ultimate Elongation at Break | % | 465 |